Bronze is an alloy consisting primarily of copper, commonly with about 12% tin and often with the addition of other metals (such as aluminium, manganese, nickel or zinc) and sometimes non-metals or metalloids such as arsenic, phosphorus or silicon. These additions produce a range of alloys that may be harder than copper alone, or have other useful properties, such as stiffness, ductility or machinability. The historical period where the archeological record contains many bronze artifacts is known as the Bronze Age.
Because historical pieces were often made of brasses (copper and zinc) and bronzes with different compositions, modern museum and scholarly descriptions of older objects increasingly use the more inclusive term "copper alloy" instead.
- Etymology 1
- History 2
Technical isssues 3
- Composition, Alloys 3.1
- Properties 3.2
- Varieties of fitness 3.3
- Industry 4.1
- Sculptures 4.2
- Musical instruments 4.3
- Medals 4.4
- Gallery 5
- See also 6
- References 7
- External links 8
- bróntion, back-formation from Byzantine Greek brontēsíon (11th century), perhaps from Brentḗsion ‘Brindisi’, reputed for its bronze; or
- early Armenian płinj "copper".
The discovery of bronze enabled people to create metal objects which were harder and more durable than previously possible. Bronze tools, weapons, armor, and building materials such as decorative tiles were harder and more durable than their stone and copper ("Chalcolithic") predecessors. Initially, bronze was made out of copper and arsenic, forming arsenic bronze, or from naturally or artificially mixed ores of copper and arsenic, with the earliest artefacts so far known coming from the Iranian plateau in the 5th millennium BCE.
It was only later that tin was used, becoming the major non-copper ingredient of bronze in the late 3rd millennium BC.
Tin bronze was superior to arsenic bronze in that the alloying process could be more easily controlled, and the resulting alloy was stronger and easier to cast. Also, unlike arsenic, metallic tin and fumes from tin refining are not toxic. The earliest tin-alloy bronze dates to 4500 BCE in a Vinča culture site in Pločnik (Serbia). Other early examples date to the late 4th millennium BC in Africa, Susa (Iran) and some ancient sites in China, Luristan (Iran) and Mesopotamia (Iraq).
Ores of copper, and the far rarer tin, are not often found together (exceptions include one ancient site in Thailand and one in Iran), so serious bronze work has always involved trade. Tin sources and trade in ancient times had a major influence on the development of cultures. In Europe, a major source of tin was England's deposits of ore in Cornwall, which were traded as far as Phoenicia in the Eastern Mediterranean.
In many parts of the world large hoards of bronze artefacts are found, suggesting that bronze also represented a store of value and an indicator of social status. In Europe large hoards of bronze tools, typically socketed axes (illustrated above), are found, which mostly show no signs of wear. With Chinese ritual bronzes, which are documented in the inscriptions they carry and from other sources, the case is very clear. These were made in enormous quantities for elite burials, and also used by the living for ritual offerings.
Though bronze is generally harder than wrought iron, with Vickers hardness of 60–258 vs. 30–80, the Bronze Age gave way to the Iron Age because iron was easier to find and easier to process into a usable grade of metal (it can be made into higher grades, but doing so takes significantly more effort and knowledge of techniques). Pure iron is soft, and the process of beating and folding sponge iron to make wrought iron removes from the metal carbon and other impurities which need to be re-introduced to improve hardness. Careful control of the alloying and tempering eventually allowed for wrought iron with properties comparable to modern steel.
Bronze was still used during the Iron Age, and has continued in use for many purposes to the modern day. Among other advantages it does not rust. The weaker wrought iron was found to be sufficiently strong for many uses. Archaeologists suspect that a serious disruption of the tin trade precipitated the transition. The population migrations around 1200–1100 BC reduced the shipping of tin around the Mediterranean (and from Great Britain), limiting supplies and raising prices.
As the art of working in iron improved, iron became cheaper, and as cultures advanced from wrought iron (typically forged by hand – wrought – by blacksmiths) to machine forged iron (typically made with trip hammers powered by water), the blacksmiths learned how to make steel, which is stronger than bronze and holds a sharper edge longer.
There are many different bronze alloys, but typically modern bronze is 88% copper and 12% tin. Alpha bronze consists of the alpha solid solution of tin in copper. Alpha bronze alloys of 4–5% tin are used to make coins, springs, turbines and blades. Historical "bronzes" are highly variable in composition, as most metalworkers probably used whatever scrap was on hand; the metal of the 12th-century English Gloucester Candlestick is bronze containing a mixture of copper, zinc, tin, lead, nickel, iron, antimony, arsenic with an unusually large amount of silver – between 22.5% in the base and 5.76% in the pan below the candle. The proportions of this mixture may suggest that the candlestick was made from a hoard of old coins. The Benin Bronzes are really brass, and the Romanesque Baptismal font at St Bartholomew's Church, Liège is described as both bronze and brass.
In the Bronze Age, two forms of bronze were commonly used: "classic bronze", about 10% tin, was used in casting; and "mild bronze", about 6% tin, was hammered from ingots to make sheets. Bladed weapons were mostly cast from classic bronze, while helmets and armor were hammered from mild bronze.
Commercial bronze (90% copper and 10% zinc) and architectural bronze (57% copper, 3% lead, 40% zinc) are more properly regarded as brass alloys because they contain zinc as the main alloying ingredient. They are commonly used in architectural applications.
Bismuth bronze is a bronze alloy with a composition of 52% copper, 30% nickel, 12% zinc, 5% lead, and 1% bismuth. It is able to hold a good polish and so is sometimes used in light reflectors and mirrors.
Plastic bronze is bronze containing a significant quantity of lead which makes for improved plasticity possibly used by the ancient Greeks in their ship construction.
Bronzes are typically very ductile alloys. By way of comparison, most bronzes are considerably less brittle than cast iron. Typically bronze only oxidizes superficially; once a copper oxide (eventually becoming copper carbonate) layer is formed, the underlying metal is protected from further corrosion. However, if copper chlorides are formed, a corrosion-mode called "bronze disease" will eventually completely destroy it. Copper-based alloys have lower melting points than steel or iron, and are more readily produced from their constituent metals. They are generally about 10 percent denser than steel, although alloys using aluminium or silicon may be slightly less dense. Bronzes are softer and weaker than steel—bronze springs, for example, are less stiff (and so store less energy) for the same bulk. Bronze resists corrosion (especially seawater corrosion) and metal fatigue more than steel and is a better conductor of heat and electricity than most steels. The cost of copper-base alloys is generally higher than that of steels but lower than that of nickel-base alloys.
Copper and its alloys have a huge variety of uses that reflect their versatile physical, mechanical, and chemical properties. Some common examples are the high electrical conductivity of pure copper, the low-friction properties of bearing bronze (bronze which has a high lead content— 6-8%), the resonant qualities of bell bronze (20% tin, 80% copper), and the resistance to corrosion by sea water of several bronze alloys.
The melting point of bronze varies depending on the ratio of the alloy components and is about 950 °C (1,742 °F). Bronze may be nonmagnetic, but certain alloys containing iron or nickel may have magnetic properties.
Varieties of fitness
Bronze, or bronze-like alloys and mixtures, were used for coins over a longer period. Bronze was especially suitable for use in boat and ship fittings prior to the wide employment of stainless steel owing to its combination of toughness and resistance to salt water corrosion. Bronze is still commonly used in ship propellers and submerged bearings.
In the 20th century, silicon was introduced as the primary alloying element, creating an alloy with wide application in industry and the major form used in contemporary statuary. Sculptors may prefer silicon bronze because of the ready availability of silicon bronze brazing rod, which allows colour-matched repair of defects in castings. Aluminium is also used for the structural metal aluminium bronze.
It is also widely used for cast bronze sculpture. Many common bronze alloys have the unusual and very desirable property of expanding slightly just before they set, thus filling in the finest details of a mould. Bronze parts are tough and typically used for bearings, clips, electrical connectors and springs.
Bronze also has very low metal-on-metal friction, making it invaluable for the building of cannon where iron cannonballs would otherwise stick in the barrel. It is still widely used today for springs, bearings, bushings, automobile transmission pilot bearings, and similar fittings, and is particularly common in the bearings of small electric motors. Phosphor bronze is particularly suited to precision-grade bearings and springs. It is also used in guitar and piano strings.
Unlike steel, bronze struck against a hard surface will not generate sparks, so it (along with beryllium copper) is used to make hammers, mallets, wrenches and other durable tools to be used in explosive atmospheres or in the presence of flammable vapors. Bronze is used to make bronze wool for woodworking applications where steel wool would discolour oak.
Various kinds of bronze are used in many different industrial applications.
Phosphor bronze is used for ships' propellers, musical instruments, and electrical contacts. Bearings are often made of bronze for its friction properties. It can be filled with oil to make the proprietary Oilite and similar material for bearings. Aluminium bronze is very hard and is used for bearings and machine tool ways.
In India, bronze sculptures from the Kushana (Chausa hoard) and Gupta periods (Brahma from Mirpur-Khas, Akota Hoard, Sultanganj Buddha) and later periods (Hansi Hoard) have been found. Indian Hindu artisans from the period of the Chola empire in Tamil Nadu used bronze to create intricate statues via the lost wax casting method with ornate detailing depicting the deities of Hinduism mostly, but also the lifestyle of the period. The art form survives to this day, with many silpis, craftsmen, working in the areas of Swamimalai and Chennai.
In antiquity other cultures also produced works of high art using bronze. For example: in Africa, the bronze heads of the Kingdom of Benin; in Europe, Grecian bronzes typically of figures from Greek mythology; in east Asia, Chinese bronzes of the Shang and Zhou dynasty—more often ceremonial vessels but including some figurine examples. Bronze sculptures, although known for their longevity, still undergo microbial degradation; such as from certain species of yeasts.
Bronze continues into modern times as one of the materials of choice for monumental statuary.
Nearly all professional cymbals are made from bronze, which gives a desirable balance of durability and timbre. Several types of bronze are used, commonly B20 bronze, which is roughly 20% tin, 80% copper, with traces of silver, or the tougher B8 bronze which is made from 8% tin and 92% copper. As the tin content in a bell or cymbal rises, the timbre drops.
Bronze is also used for the windings of steel and nylon strings of various stringed instruments such as the double bass, piano, harpsichord, and the guitar. Bronze strings are commonly reserved on pianoforte for the lower pitch tones, as they possess a superior sustain quality to that of high-tensile steel.
Bronzes of various metallurgical properties are widely used in struck idiophones around the world, notably bells, singing bowls, gongs, cymbals and other idiophones from Asia. Examples include Tibetan singing bowls, temple bells of many sizes and shapes, gongs, Javanese gamelan and other bronze musical instruments. The earliest bronze archeological finds in Indonesia date from 1–2 BCE, including flat plates probably suspended and struck by a wooden or bone mallet. Ancient bronze drums from Thailand and Vietnam date back 2,000 years. Bronze bells from Thailand and Cambodia date back to 3,600 BCE.
Some companies are now making saxophones from phosphor bronze (3.5 to 10% tin and up to 1% phosphorus content). Bell bronze is used to make the tone rings of many professional model banjos. The tone ring is a heavy (usually 3 lbs.) folded or arched metal ring attached to a thick wood rim, over which a skin, or most often, a plastic membrane (or head) is stretched - it is the bell bronze that gives the banjo a crisp powerful lower register and clear, bell-like treble register-especially in bluegrass music.
As with coins, bronze has been used in the manufacture of various types of medals for centuries, and are known in contemporary times for being awarded for third place in sporting competitions and other events. The later usage was in part attributed to the choices of gold, silver and bronze to represent the first three Ages of Man in Greek mythology: the Golden Age, when men lived among the gods; the Silver age, where youth lasted a hundred years; and the Bronze Age, the era of heroes, and was first adopted at the 1904 Summer Olympics. At the 1896 event, silver was awarded to winners and bronze to runners-up, while at 1900 other prizes were given, not medals.
- Art object
- Bronze and brass ornamental work
- Chinese bronze inscriptions
- Dezincification Resistant Brass
- French Empire mantel clock
- List of copper alloys
- Seagram Building
- UNS C69100
- Yoruba art
- Henry and Renée Kahane, "Byzantium's Impact on the West: The Linguistic Evidence", Illinois Classical Studies 06 (2) 1981, p. 395.
- Originally M.P.E. Berthelot, "Sur le nom du bronze chez les alchimistes grecs", in Revue archéologique, 1888, pp. 294-8.
- Originally Karl Lokotsch, Etymologisches Wörterbuch der europäischen Wörter orientalischen Ursprungs. (Heidelberg: Carl Winter’s Universitätsbuchhandlung, 1927), p. 1657.
- Wolfgang Pfeifer, ed., Etymologisches Wörterbuch des Deutschen, s.v. "Bronze" (Munich: Deutscher Taschenbucher Vertrag, 2005).
- Brett Kaufman, "Metallurgy and Archaeological Change in the Ancient Near East", Backdirt: Annual Review 2011, p. 86.
- History of Africa#Metallurgy
- Precious Metals: Bronze Jewelry. Allaboutgemstones.com. Retrieved on 2012-06-09. Under construction Oct 2015
- Smithells Metals Reference Book, 8th Edition, ch. 22
- Clayton E. Cramer. What Caused The Iron Age? claytoncramer.com. December 10, 1995
- Oleg D. Sherby and Jeffrey Wadsworth. Ancient Blacksmiths, the Iron Age, Damascus Steels, and Modern Metallurgy. Tbermec 2000, Las Vegas, Nevada December 4–8, 2000. Retrieved on 2012-06-09.
- Knapp, Brian. (1996) Copper, Silver and Gold. Reed Library, Australia.
- plastic bronze definition of plastic bronze in the Free Online Encyclopedia
- The Belgammel Ram, a Hellenistic-Roman Bronze Proembolion Found off the Coast of Libya: test analysis of function, date and metallurgy, with a digital reference archive
- Resources: Standards & Properties - Copper & Copper Alloy Microstructures: Phosphor Bronze
- Resources: Standards & Properties - Copper & Copper Alloy Microstructures: Aluminum Bronzes
- Indian bronze masterpieces: the great tradition : specially published for the Festival of India, Asharani Mathur, Sonya Singh, Festival of India, Brijbasi Printers, Dec 1, 1988
- for a translation of his inscription see the appendix in Stephanie Dalley, (2013) The Mystery of the Hanging Garden of Babylon: an elusive World Wonder traced, OUP. ISBN 978-0-19-966226-5
- McCreight, Tim. Metals technic: a collection of techniques for metalsmiths. Brynmorgen Press, 1992. ISBN 0-9615984-3-3
- LaPlantz, David. Jewelry – Metalwork 1991 Survey: Visions – Concepts – Communication: S. LaPlantz: 1991. ISBN 0-942002-05-9
- Media related to at Wikimedia Commons
- Bronze bells
- "Lost Wax, Found Bronze": lost-wax casting explained
- Viking Bronze – Ancient and Early Medieval bronze casting